Alkyl polyglycosides (APGs) are new biodegradable surfactants, non-toxic, synthesized from abundant renewable sources, potentially more appropriate than anionic surfactants. A range of glycosides denoted APG-Cy was synthesized by the Köenig-Knorr reaction using C10, C16 and C18 alcohols and derived from the degradation of amylose from English potato. The molecular structures of the glycosides were characterized by Nuclear Magnetic Resonance (1H and 13C NMR) together with Infrared Spectroscopy (FTIR) and Gel Permeation Chromatography (GPC). The study by NMR allowed the junctions between hydrophilic head groups and hydrophobic tail-groups to be characterized in detail. Conformation of the glycosidic units is 4C1 type with a b anomeric configuration. The formation of glycosides with five glucose rings linked to the alkyl chain was confirmed by 1H NMR and GPC. Liquid crystals identified by the presence of double melting points were observed by Differential Scanning Calorimetry (DSC) showing thermotropic properties. The surface tension (γ) and critical micelle concentration (cmc) were determined by du Noüy method, noting that increasing the length of alkyl chain led to the expected reduction in the cmc. The energies of adsorption and micellization processes calculated from isotherms γ versus ln c (g.dm-3) indicate cooperativeness of hydrophilic and hydrophobic groups.

The surfactants were synthesized by condensing the obtained oligosaccharides of amylose and alkyl phenols extracted from the natural cashew nut shell liquid (nCNSL). The Nuclear Magnetic Resonance (NMR) and Fourier Transform Infrared Spectroscopy (FTIR) data showed aromatic ring bands, glycosidic rings, olefins and paraffins. The Nuclear Overhauser Effect Spectroscopy (NOESY) experiments showed that the conformation of the glycosidic units is of the type 4C1 with an α anomeric configuration. The values of Gibbs free energy of micellization (ΔGºmic) indicate that the spontaneity of formed micelles are cardanyl oligoglycosides > cardyl oligoglycosides > anacardyl oligoglycosides. The surface tension (γ) measurements showed that critical micelle concentration (cmc) values were low for surfactants. The study γ versus lnc (g dm-3) indicated that the aggregation behavior of the surfactants is dependent on their structural characteristics, as well as their thermal behavior. The area per molecule (A) values indicates that cardyl oligoglycosides are likely to form aggregates smaller than cardanyl oligoglycosides and anacardyl oligoglycosides. The critical packing parameter (cpp) indicates that the aggregates are of the vesicles and bilayers.

A novel superabsorbent hydrogel (SH) composite based on a poly(acrylamide-co-acrylate) matrix filled with nontronite (NONT), a Fe(III)-rich member of the smectite group of clay minerals, is described in this manuscript. A variety of techniques, including FTIR, XRD, TGA, and SEM/EDX, were utilized to characterize this original composite. Experimental data confirmed the SH composite formation and suggested NONT was completely dispersed in the polymeric matrix. Additionally, NONT improved the water uptake capacity of the final material, which exhibited fast absorption, low sensitivity to the presence of salt, high water retention and a pH sensitive properties. These preliminary data showed that the original SH composite prepared here possesses highly attractive properties for applications in areas such as the agriculture field, particularly as a soil conditioner.

Superabsorbent hydrogels based on poly (acrylamide-co-acrylate) and different kaolins, were prepared by free-radical aqueous copolymerization. FTIR and WAXS techniques were employed for characterization of a series of hydrogels, obtained by varying the percentage of clay, crosslinking and constitution of kaolin. The water absorbency at equilibrium (Weq) decreased with increasing clay content and the amount of crosslinking agent. Superabsorbent hydrogel (Weq > 1084 g H2O/g gel) was obtained as 10 wt% of white kaolin and 0.05 mol% of crosslinking agent were used. The hydrogel proved sensitive to pH variation and the presence of salts.

Cashew nut shell liquid (CNSL) is a by-product of the cashew kernel industry, applied mainly to produce polymeric derivatives. The technical CNSL (CNSLT) was obtained industrially, extracted by roasting the cashew nut shells at temperatures between 180 and 200 ºC. Two methods were used to produce natural CNSL. For the extraction of CNSLNP, the cashew nut shells were pressed at room temperature. CNSLNS was extracted in hexane at room temperature and recovered at 50 ºC. A comparison was made of the composition determined by HPLC and properties generated by viscosity measurements and also by TG, DSC and IPDT (integral procedural decomposition temperature). Natural CNSLs displayed higher content of cardol and anacardic acid and lower percentage of cardanol than CNSLT. The higher content of cardanol in CNSLNS was the major difference between natural CNSLs. CNSLNP had higher levels of impurity, higher viscosity, lower thermoxidative stabilities and lower ebullition temperature. The CNSL obtained by cold solvent extraction and recovery at 50 ºC better preserves the original properties of the liquid.